Tange velum velamentum vitreum, tange tabula vitrum, operculum Lens
Technical data
vitrum aluminosilicatum | Nitri vitreum calcis | |||||
Type | corning muta vitrum | dragontrail vitrum | Schott Xensat | panda vitrum | NEG T2X-1 glass | supernatet vitrum |
Crassitudo | 0.4mm,0.5mm,0.55mm,0.7mm 1mm,1.1mm,1.5mm,2mm | 0.55mm,0.7mm,0.8mm 1.0mm,1.1mm,2.0mm | 0.55mm,0.7mm 1.1mm | 0.7mm,1.1mm | 0.55mm,0.7mm 1.1mm | 0.55mm,0.7mm,1.1mm,2mm 3mm,4mm,5mm,6mm |
Confortatus eget | DOL≥ 40um CS≥700Mpa | DOL≥ 35um CS≥650Mpa | DOL≥ 35um CS≥650Mpa | DOL≥ 32um CS≥600Mpa | DOL≥ 35um CS≥650Mpa | DOL≥ 8um CS≥450Mpa |
duritia | ≥9H | ≥9H | ≥7H | ≥7H | ≥7H | ≥7H |
Transmittance | >92% | >90% | >90% | >90% | >90% | >89% |
Superficies curatio: Anti fulgor coating, anti vestis reflectiva, anti fingerprints, "prolixa tunica in promptu est.
Optio temperata: Thermaliter temperatur, calor confortatur, chemica roboratur (chemice temperatur).
Processing
Type operculum Vitri
1. Aluminosilica vitrum refert ad vitrum cum silica et alumina tanquam principales partes, in quibus alumina contenta plus quam 20% attingere potest.Coordinatio numerus aluminii ion dependet ab R2O (oxide metallico alcali) contento.
Felis Vitrum a corninge unum vitreum aluminosilicate kinf est. ob hanc praestantiam in.
Superior nodus resistens boni chemicae stabilitatis;
electrica velit
mechanica vires
humilis scelerisque expansionem coefficiens
caliditas viscositas.
Magno pretio
Late in genere tactus velorum et telephonicorum, vel aliis machinis portatilis, late adhibetur.
Vitreum calcis nitri, vitrei forma communissimum, vilis est, chemica stabilis, rationabiliter dura, et vitrum perquam operabile, satis est ad postulata fundamentalia, quae maxime popularem et late usum in tabellis tactus variis in applicatione faciunt.
STEPHANT VITREI VS , caloris vitrei confirmati, vitri temperari vitri.
Quae differentia est inter scelerisquely temperatam et chymicam vitro roboratam.