Ito vitrum emi protegens et touchscreens

Features:

Consuetudo magnitudine et figura

Princeps corporis densitate coating

Imprimis resistentia electrica

resistentia vitro (resistentia inter CL et 500 ohms)

Ordinarius speculum (resistere inter LX et CL ohms)

Minimum resistentia vitrum (resistere minus quam LX ohms)

Princeps environmental et temperatus stabilitas

Optimum electrica conductivity et diaphanum opticum

Coing uniformitas

Facultatem defendendi electromagneticorum Agri

Deponi potest in tenues pelliculas

Scelerisque ac chemica stabilis

Petere quote

Product Detail

Product Tags

Products Pics

ITO vitrum bitumen conductivum fit patula dioxide pii (SiO2) et oxydi indium stagni (vulgo ITO) iacuit magnetron technologia putris vitreae sub conditione vitreo sub condicione prorsus vacuato, faciei conductiva lita faciens, ITO mixtum metallicum cum bono perspicuo et possessiones conductas.

Tactus vitrum protegens

2mm ito coating touch panel cover vitri

3mm

4mm ito vitreum pro capacitivo tactus switch

Technical data

ITO crassitudine vitreo	0.4mm,0.5mm,0.55mm,0.7mm,1mm,1.1mm,2mm,3mm,4mm
resistentia	3-5Ω	7-10Ω	12-18Ω	20-30Ω	30-50Ω	50-80Ω	60-120Ω	100-200Ω	200-500Ω
crassitudine efficiens	2000-2200Å	1600-1700Å	1200-1300Å	650-750Å	350-450Å	200-300Å	150-250Å	100-150Å	30-100Å

Speculum resistentiae
Resistentia type	humilis resistentia	normalis resistentia	magno resistentia
Definition	<60Ω	60-150Ω	150-500Ω
Applicationem	Repugnantia vitrea magna plerumque adhibentur ad tutelam electrostaticam et tactum productionis screen	Vitreum resistentia ordinaria plerumque adhibetur pro TN specie liquida cristallinae ostentationis et electronic anti-incursio (EMI protegens)	Vitrum humilis resistentia plerumque adhibetur in STN liquido crystallo exhibito et ambitu tabulae pellucidae

Eget test et reliability test
tolerantia	±0.2mm
Warpage	crassitudine0.55mm, warpage≤0.15% crassitudine0.7mm, warpage≤0.15%
ZT vertical	≤1°
duritia	>7H
Abrasion test coating	0000# ferro lanae cum 1000gf.6000cycles,40cycles/min
Anti corrsion test (sal imbre test)	NaCL retrahitur 5%: Temperature: 35°C Experimentum temporis: 5min resistentia change≤10%
Repugnantia Umor test	60.90% RH.XLVIII horis resistentia change≤10%
Acidum resistentia test	HCL concentration:6%, Temperature: 35°C Experimentum temporis: 5min resistentia change≤10%
Alkali resistentia test	Retrahitur NaOH: 10%, Temperature: 60°C Experimentum temporis: 5min resistentia change≤10%
Themal stabilitatis	Temperature: CCC° calefactio temporis: 30min resistentia change≤300%

Processing

Ito Glass flow Chart

Est Sio2 deauratae sub Ito Coating, Quid est?

Si02 iacuit:
(1) Munus iacuit SiO2:
Praecipuum propositum est ne metalla in calcii nitri substratis diffundantur in strato ITO.Conductu ITO iacuit afficit.

(2) Crassitudo pelliculae SiO2 iacuit;
Crassitudo cinematographica vexillum plerumque 250± 50

(3) Alia membra in strato SiO2:
Solet, ut vitrei ITO transmissio emendaretur, proportio certa SiN4 in SiO2 emittitur.

Utrumque Vitrum Conducit, Quid est Vitrum Fto?