1.ultra vitrum purum habet multum inferiorem vitri sui explosionis ratio
Definition of auto-explosionis: Vitri temperati sui explosio est phaenomenon comminuens quae sine vi externa fit.
Principium explosionis centrum est et radiatim in circumfusum diffunditur.In exordio sui explosionis duo fragmenta relative magna erunt cum proprietatibus "papilii macularum".
Causae explosionis sui: Explicatio vitri temperati sui saepe causatur ex existentia nonnullorum lapidum minutorum in scheda vitri temperati originali.Temperatus cristallinus status calidissimus (a-NiS) est "gelidus" in productione vitrea et in temperie ambiente servatur.In vitro temperato, cum hic status crystallinus summus temperatus non stabilis sit in cella temperie, paulatim in statum normalem crystallinum (B-NiS) cum tempore transformabit, et cum quadam dilatatione voluminis erit (2~). 4% dilatatio) in transmutatione.;Si lapis sita est in area distrahentes in vitro temperato, haec crystalli periodus transmutatio processus saepe efficit ut speculum temperatum repente frangat, quod est quod plerumque vitri temperati explosionem sui ipsius appellare consuevimus.
Sui explosio rate of ultra vitrum temperatum perspicuum: Quia ultra vitreum vitreum altum puritatis chalcitis rudis materiae utitur, immunditia compositio ad minimum redigitur, et compositio niS correspondens multo humilior est quam vitri ordinarii innatantia, ita sui ipsius. -explosio rate attingere potest intra 2/, circa 15 tempora inferiora cum 3‰ auto-explosione rate ordinaria vitro perspicuo.
2. Color constantia
Cum ferrum in materia rudis contentum tantum 1/10 vel etiam minus quam vitri ordinarii, ultra-lucidum vitreum minus viridis necem in luce visibili quam vitreo ordinario haurit, constantiam vitrei coloris procurans.
3. Ultra vitrum perspicuum habet maiorem transmissionem et coefficientem solarem.
| ultra patet vitrum parametri | |||||||||||||
| Crassitudo | transmissio | Reflexio | solaris radiatio | colorum coefficiens | Ug | soundproofing | UV transmissio | ||||||
| recta penatrating | reputans | effusio | total | shortwave | longwave | total | (W/M2k) | Rm (dB* | Rw（dB) | ||||
| 2mm | 91.50% | 8% | 91% | 8% | 1% | 91% | 1.08 | 0.01 | 1.05 | 6 | 25 | 29 | 79% |
| 3mm | 91.50% | 8% | 90% | 8% | 1% | 91% | 1.05 | 0.01 | 1.05 | 6 | 26 | 30 | 76% |
| 3.2mm | 91.40% | 8% | 90% | 8% | 2% | 91% | 1.03 | 0.01 | 1.05 | 6 | 26 | 30 | 75% |
| 4mm | 91.38% | 8% | 90% | 8% | 2% | 91% | 1.03 | 0.01 | 1.05 | 6 | 27 | 30 | 73% |
| 5mm | 91.30% | 8% | 90% | 8% | 2% | 90% | 1.03 | 0.01 | 1.03 | 6 | 29 | 32 | 71% |
| 6mm | 91.08% | 8% | 89% | 8% | 3% | 90% | 1.02 | 0.01 | 1.03 | 6 | 29 | 32 | 70% |
| 8mm | 90.89% | 8% | 88% | 8% | 4% | 89% | 1.01 | 0.01 | 1.02 | 6 | 31 | 34 | 68% |
| 10mm | 90.62% | 8% | 88% | 8% | 4% | 89% | 1.01 | 0.02 | 1.02 | 6 | 33 | 36 | 66% |
| 12mm | 90.44% | 8% | 87% | 8% | 5% | 88% | 1.00 | 0.02 | 1.01 | 6 | 34 | 37 | 64% |
| 15mm | 90.09% | 8% | 86% | 8% | 6% | 87% | 0.99 | 0.02 | 1.00 | 6 | 35 | 38 | 61% |
| 19mm | 89.73% | 8% | 84% | 8% | 7% | 86% | 0.97 | 0.02 | 0.99 | 6 | 37 | 40 | 59% |
4. ultra vitrum perspicuum habet transmissionem UV inferiorem
| patet vitrum parametri | |||
| Crassitudo | transmissio | Reflexio | UV transmissio |
| 2mm | 90.80% | 10% | 86% |
| 3mm | 90.50% | 10% | 84% |
| 3.2mm | 89.50% | 10% | 84% |
| 4mm | 89.20% | 10% | 82% |
| 5mm | 89.00% | 10% | 80% |
| 6mm | 88.60% | 10% | 78% |
| 8mm | 88.20% | 10% | 75% |
| 10mm | 87.60% | 10% | 72% |
| 12mm | 87.20% | 10% | 70% |
| 15mm | 86.50% | 10% | 68% |
| 19mm | 85.00% | 10% | 66% |
5. ultra vitrum limpidum difficultatem productionis altiorem habet, sic sumptus vitrei claris altior est
Ultra vitrum clarum quale requisitum habet ad vicus arenae ingredientes, etiam altas requiruntur ad contentum ferreum, chalcitis naturalis ultra-album vicus arena vix est, et ultra vitrum clarum relative altum technologicum habet, productio temperantia difficultatem faciens. est circa 2 tempora altior quam vitro puro.